Effect of Different Heat Treatments on Mechanical Properties of Laser Sintered Additive Manufactured Parts

[+] Author Affiliations
Sagar Sarkar, Cheruvu Siva Kumar, Ashish Kumar Nath

Indian Institute of Technology, Kharagpur, Kharagpur, India

Paper No. MSEC2017-2769, pp. V002T01A009; 7 pages
  • ASME 2017 12th International Manufacturing Science and Engineering Conference collocated with the JSME/ASME 2017 6th International Conference on Materials and Processing
  • Volume 2: Additive Manufacturing; Materials
  • Los Angeles, California, USA, June 4–8, 2017
  • Conference Sponsors: Manufacturing Engineering Division
  • ISBN: 978-0-7918-5073-2
  • Copyright © 2017 by ASME


One of the most popular additive manufacturing processes is laser based direct metal laser sintering process which enables us to make complex three dimensional parts directly from CAD models. Due to layer by layer formation, parts built in this process tend to be anisotropic in nature. Suitable heat treatment can reduce this anisotropic behaviour by changing the microstructure. Depending upon the applications, a wide range of mechanical properties can be achieved between 482–621° C temperature for precipitation-hardened stainless steels. In the present study effect of different heat treatment processes, namely solution annealing, ageing and overaging, on tensile strength, hardness and wear properties has been studied in detail. Suitable metallurgical and mechanical characterization techniques have been applied wherever required, to support the experimental observations. Results show H900 condition gives highest yield strength and lowest tensile strain at break whereas solution annealing gives lowest yield strength and as-built condition gives highest tensile strain at break. SEM images show that H900 and H1150 condition produces brittle and ductile morphology respectively which in turn gives highest and lowest hardness value respectively.XRD analysis shows presence of austenite phases which can increase hardness at the cost of ductility. Average wear loss for H900 condition is highest whereas it is lowest for solution annealed condition. Further optical and SEM images have been taken to understand the basic wear mechanism involved.

Copyright © 2017 by ASME



Interactive Graphics


Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In