High Temperature Interfacial Adhesion Strength Measurement in Electronic Packaging Using the Double Cantilever Beam Method

[+] Author Affiliations
Santosh Sankarasubramanian, Kyle Yazzie, Vijay Subramanian, Edvin Cetegen, David McCoy, Pramod Malatkar

Intel Corporation, Chandler, AZ

Jaime Cruz

University of Texas at El Paso, El Paso, TX

Vaasavi Sundar

Arizona State University, Tempe, AZ

Paper No. IMECE2016-67007, pp. V010T13A047; 7 pages
doi:10.1115/IMECE2016-67007
From:
  • ASME 2016 International Mechanical Engineering Congress and Exposition
  • Volume 10: Micro- and Nano-Systems Engineering and Packaging
  • Phoenix, Arizona, USA, November 11–17, 2016
  • Conference Sponsors: ASME
  • ISBN: 978-0-7918-5064-0
  • Copyright © 2016 by ASME

abstract

Advanced microelectronic packages utilize a multitude of materials with dramatically different mechanical properties. Delamination occurring at the interfaces between these materials, due to poor adhesion and/or moisture exposure, is an important failure mode affecting the thermomechanical reliability of the package. The adhesion strength of these interfaces is a critical mechanical property that plays a role in the reliability performance of these packages. A good adhesion strength metrology is required to perform material selection and enable assembly process optimization in order to avoid the need for expensive assembly builds, followed by reliability testing which leads to long development times. This paper discusses the use of the Double Cantilever Beam (DCB) method for characterizing the adhesion strength of interfaces in advanced microelectronic packages at both room and high temperatures. Previous work in this area was focused only on room temperature testing. However, in order to characterize the adhesion strength of these interfaces at elevated temperatures seen during package assembly and reliability testing, an environmental chamber was designed and fabricated to rapidly and uniformly heat the DCB samples for testing at high temperatures. Depending on the interface tested and the testing temperature, DCB samples failed in one of three fail modes: (1) adhesive (at the interface), (2) cohesive (within the adhesive layer), and (3) brittle cracking of the substrate. Two case studies describing high temperature DCB testing on silicon-capillary underfill samples are presented. With adhesive failure being the desired fail mode in order to rank order materials and processes, it was found that for the underfills tested in this study, the DCB samples failed cohesively within the underfill at room temperature but started failing adhesively at temperatures near 150°C. Adhesion strength also showed a clear degradation with temperature. It is suspected that the change in failure mode from cohesive to adhesive with increasing temperature is due to competing trends of degradation in cohesive strength of the underfill versus degradation in adhesive strength of the interface with temperature.

Copyright © 2016 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In