Microstructural Analysis of Spall Damage Nucleation and Growth in Multicrystalline Titanium

[+] Author Affiliations
Elizabeth V. Fortin, Leda Wayne, Pedro D. Peralta

Arizona State University, Tempe, AZ

Andrew D. Brown

University of New South Wales, Campbell, Australia

Paper No. IMECE2016-67667, pp. V009T12A044; 6 pages
doi:10.1115/IMECE2016-67667
From:
  • ASME 2016 International Mechanical Engineering Congress and Exposition
  • Volume 9: Mechanics of Solids, Structures and Fluids; NDE, Diagnosis, and Prognosis
  • Phoenix, Arizona, USA, November 11–17, 2016
  • Conference Sponsors: ASME
  • ISBN: 978-0-7918-5063-3
  • Copyright © 2016 by ASME

abstract

Shock loading is a dynamic condition that can lead to material failure and deformation modes at the microstructural level such as cracking, void nucleation and growth, and spallation. Knowledge of shock loading and spall failure is of great benefit to understanding ballistic impact in military vehicles and armor, crash impacts in automobiles, space vehicles, and satellite loadings, and geological events such as earthquakes. Furthermore, studying material failure at the microstructural level is important to understand macroscale behavior. Spallation, the nucleation, growth, and coalescence of voids, is a phenomenon where variability at the microscale can affect overall response. By analyzing incipient and intermediate damage patterns at and around interfaces and boundaries on the microstructural level, can help further our understanding of the process leading to damage and provide insight on how to develop stronger structures that can withstand impacts and rapid crack propagation. Most of the existing work has looked into the effect of grain boundaries in spall damage for body and face centered cubic (BCC, FCC) materials, but research is still lacking on grain boundary effects in spall damage in hexagonal close packed materials, such as titanium. Samples of high purity Ti were heat treated to obtain large grains, averaging 250 microns in size (multicrystals), in order to isolate grain boundary effects. These multicrystals were shocked using laser-launched flyer plates at the Trident laser at Los Alamos National Laboratory (LANL) and monitored using a velocity interferometry system for any reflector (VISAR). Pressures used were 5–8 GPa. Samples were soft recovered and cross-sectioned to perform quantitative characterization of damage. Spallation damage observed in the titanium targets was characterized using electron backscattering diffraction (EBSD), optical microscopy, and scanning electron microscopy (SEM) to gather information on the crystallographic characteristics of damage nucleation sites, with emphasis on grain boundaries and grain orientations that lead to damage localization. Initial results show that damage localized along grain boundaries, and the damage mode switched from intergranular to transgranular where grains were larger than average.

Copyright © 2016 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In