The Genesis of Tool Wear in Machining

[+] Author Affiliations
Trung Nguyen

Hanoi University of Science and Technology, Hanoi, Vietnam

Kyung-Hee Park

KITECH, Cheonan-si, Korea

Xin Wang

Tshinghua University, Beijing, China

Jorge Olortegui-Yume

National University of Trujillo, Trijillo, Peru

Tim Wong

Fullerton School District, Fullerton, CA

David Schrock

Eaton Corporation, Marshall, MI

Wonsik Kim

LTD R&D, Anyang, Korea

Patrick Kwon

Michigan State University, East Lansing, MI

Bruce Kramer

National Science Foundation, Arlington, VA

Paper No. IMECE2015-52531, pp. V015T19A013; 11 pages
doi:10.1115/IMECE2015-52531
From:
  • ASME 2015 International Mechanical Engineering Congress and Exposition
  • Volume 15: Advances in Multidisciplinary Engineering
  • Houston, Texas, USA, November 13–19, 2015
  • Conference Sponsors: ASME
  • ISBN: 978-0-7918-5758-8
  • Copyright © 2015 by ASME

abstract

This paper presents a series of experimental and theoretical efforts that we have made in unraveling the tool wear mechanisms under steady state conditions in machining for the last few decades. Two primary modes of steady state tool wear considered in this paper are flank and crater wear. We preface this paper by stating that flank wear is explained as abrasive wear due to the hard phases in a work material while crater wear is a combination of abrasive wear and generalized dissolution wear which encompasses both dissolution wear as well as diffusion wear. However, the flank wear was not a function of the abrasive cementite content when turning low alloy steels with pearlitic microstructures. The machined surfaces of these alloys are examined to confirm the phase transformation (ferrite to austenite), which diminishes the effect of cementite content. In particular, the cementite phase present in low alloy steels dissociates and diffuses into the transformed austenitic phase during machining. Dissolution wear is claimed to describe the behavior of crater wear at high cutting speeds. The original dissolution mechanism explains the crater wear in the machining of ferrous materials and nickel alloys at high cutting speeds, but the generalization of the dissolution wear is necessary for titanium alloys. In machining titanium alloys, the original dissolution mechanism did not show a good correlation with experimental results; generally the diffusivity of the slowest diffusing tool constituent in titanium limits the wear rate. The phase transformation from alpha (HCP) to beta (BCC) phases can also take place in machining titanium alloys, which drastically increases the crater wear due to the few orders of magnitude increase in diffusivity. The most puzzling issue is however the presence of the scoring marks even though no hard inclusion is typically present in titanium alloys. This is finally explained by the heterogeneity in the microstructure due to the anisotropic hardness of alpha (HCP) phase (the hardness in c-direction is 50% higher than the hardness in other directions) and the presence of lamellar microstructure (alternating layers of alpha and beta). The lamellar microstructure has not only the in-plane anisotropic hardness but also a greater hardness than other phases. Even though we cannot claim to fully understand the physics behind tool wear, our combined approaches have unveiled some elementary wear mechanisms.

Copyright © 2015 by ASME
Topics: Wear , Machining

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In