Heavy Haul Coal Car Wheel Load Environment: Rolling Contact Fatigue Investigation

[+] Author Affiliations
Sabri Cakdi, Scott Cummings

Transportation Technology Center, Inc., Pueblo, CO

John Punwani

Federal Railroad Administration, Washington, DC

Paper No. JRC2015-5640, pp. V001T02A005; 6 pages
  • 2015 Joint Rail Conference
  • 2015 Joint Rail Conference
  • San Jose, California, USA, March 23–26, 2015
  • Conference Sponsors: Rail Transportation Division
  • ISBN: 978-0-7918-5645-1
  • Copyright © 2015 by ASME


Railway wheels and rails do not achieve full wear life expectancy due to the combination of wear, plastic deformation, and surface, subsurface, and deep subsurface cracks. Sixty-seven percent of wheel replacement and maintenance in North America is associated with tread damage [1].

Spalling and shelling are the two major types of wheel tread damage observed in railroad operations. Spalling and slid flat defects occur due to skidded or sliding wheels caused by, in general, unreleased brakes. Tread shelling (surface or shallow subsurface fatigue) occurs due to cyclic normal and traction loads that can generate rolling contact fatigue (RCF). Shelling comprises about half of tread damage related wheel replacement and maintenance. The annual problem size associated with wheel tread RCF is estimated to be in the tens of millions of dollars. The total cost includes maintenance, replacement, train delays and fuel consumption.

To study the conditions under which RCF damage accumulates, a 36-ton axle load aluminum body coal car was instrumented with a high accuracy instrumented wheelset (IWS), an unmanned data acquisition (UDAC) system, and a GPS receiver. This railcar was sent to coal service between a coal mine and power plant, and traveled approximately 1,300 miles in the fully loaded condition on each trip. Longitudinal, lateral, and vertical wheel-rail forces were recorded continuously during four loaded trips over the same route using the same railcar and instrumentation. The first two trips were conducted with non-steering 3-piece trucks and the last two trips were conducted with passive steering M-976 compliant trucks to allow comparison of the wheel load environment and RCF accumulation between the truck types. RCF initiation predictions were made using “Shakedown Theory” [2]. Conducting two trips with each set of trucks allowed for analysis of the effects of imbalance speed conditions (cant deficiency or excess cant) at some curves on which the operating speeds varied significantly between trips.

Copyright © 2015 by ASME



Interactive Graphics


Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In