Application of Weibull Stress Criterion to Brittle Fracture Assessment of HAZ-Notched Welds With Residual Stress

[+] Author Affiliations
Yusuke Seko, Yasuhito Imai, Masaki Mitsuya

Tokyo Gas Co., Ltd., Yokohama, Kanagawa, Japan

Noritake Oguchi

Tokyo Gas Co., Ltd., Tokyo, Japan

Fumiyoshi Minami

Osaka University, Suita, Osaka, Japan

Paper No. IPC2014-33731, pp. V003T07A058; 10 pages
doi:10.1115/IPC2014-33731
From:
  • 2014 10th International Pipeline Conference
  • Volume 3: Materials and Joining; Risk and Reliability
  • Calgary, Alberta, Canada, September 29–October 3, 2014
  • Conference Sponsors: Pipeline Division
  • ISBN: 978-0-7918-4612-4
  • Copyright © 2014 by ASME

abstract

This paper presents a method for estimating the brittle fracture limit of a weld with a notch in the heat-affected zone (HAZ) and residual stress based on the Weibull stress criterion. A constraint loss correction procedure using the Weibull stress criterion is specified in ISO 27306. However, this standard is applicable only to structural steel components with defects, not to welded joints. Therefore, we conducted fracture tests and finite element analyses to propose a new evaluation method for welded structural components.

In this study, three-point bending (3PB) tests and wide-plate (WP) tension tests of HAZ-notched welds made of 780-MPa-class high-strength steel were conducted at −40°C. Brittle fractures occurred in the HAZ regions of all the specimens, and the critical crack tip opening displacement (CTOD) values obtained in the 3PB and WP tests were approximately 0.02–0.07 mm and 0.08–0.11 mm, respectively. The minimum critical CTOD of the WP specimen fracturing at the coarse-grained region of the HAZ (CGHAZ) was approximately four times that of the 3PB specimen. These results confirmed that the difference of specimen geometry affects the brittle fracture resistance of a HAZ-notched weld with residual stress. Hence, the assessment of the brittle fracture limit of a welded structural component with a defect obtained by the fracture toughness of a 3PB specimen would be excessively conservative.

The effects of specimen geometry, residual stress, crack-front shape and HAZ microstructure classification on the Weibull stress were investigated to clarify the difference of experimental critical CTOD for 3PB and WP by using a finite element analysis. The results of this analysis showed that the Weibull stress of WP specimen was larger than one of 3PB specimen in all CTOD region due to difference of geometry. The welding residual stress increased the Weibull stress only for WP. Compressive residual stress and crack front shape for 3PB specimen did not affect the Weibull stress. The difference of HAZ microstructure distribution for same welded joint affects the Weibull stress for 3PB and WP specimens.

Finally, it was confirmed that the brittle fracture limit of a HAZ-notched weld with residual stress could be predicted from the Weibull stress criterion because critical CTOD of WP specimens predicted by critical CTOD of 3PB specimens fracturing at the CGHAZ included critical CTOD of WP specimens obtained by experiments.

Copyright © 2014 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In