Improvement in Fatigue Limit by Shot Peening for High-Strength Steel Containing Crack-Like Surface Defect: Influence of Surface Crack Aspect Ratio

[+] Author Affiliations
Makiko Nakagawa, Koji Takahashi, Toshio Osada

Yokohama National University, Yokohama, Japan

Paper No. PVP2013-97839, pp. V005T11A025; 7 pages
doi:10.1115/PVP2013-97839
From:
  • ASME 2013 Pressure Vessels and Piping Conference
  • Volume 5: High-Pressure Technology; ASME NDE Division; Rudy Scavuzzo Student Paper Symposium
  • Paris, France, July 14–18, 2013
  • Conference Sponsors: Pressure Vessels and Piping Division, Nondestructive Evaluation Engineering Division
  • ISBN: 978-0-7918-5569-0
  • Copyright © 2013 by ASME

abstract

The effect of shot peening (SP) on the bending fatigue limit of high-strength steel (SUP9A) containing a semi-elliptical surface slit was investigated. SP was conducted on specimens containing a semi-elliptical surface slit with an aspect ratio (a/c) of 0.4, where a was the crack depth (a = 0.1, 0.2, and 0.3 mm) and c was half the surface length of the crack. Bending fatigue tests were carried out under a stress ratio R equal to 0. The results showed that the fatigue limit of the shot-peened specimens with slits having a depth of less than 0.2 mm was almost the same as that of the shot-peened specimens without slits. Meanwhile, some of the specimens fractured at the surface in areas other than the slit. Thus, the maximum depth of the slit that could be rendered harmless by SP was 0.2 mm. The maximum depths of cracks with various aspect ratios that could be rendered harmless by SP were predicted, assuming that the cracks were arrested when the apparent stress intensity factor at the slit tip was less than the threshold stress intensity factor of the material. The estimated values were in good agreement with the experimental values. A harmless crack assessment diagram was proposed based on this estimation method.

Copyright © 2013 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In