Experimental Study of Fatigue Crack Overload Retardation in X80 Grade Steel

[+] Author Affiliations
Qingquan Duan, Hong Zhang, Feng Yan

China University of Petroleum - Beijing, Beijing, China

Paper No. IPC2008-64177, pp. 285-289; 5 pages
doi:10.1115/IPC2008-64177
From:
  • 2008 7th International Pipeline Conference
  • 2008 7th International Pipeline Conference, Volume 2
  • Calgary, Alberta, Canada, September 29–October 3, 2008
  • Conference Sponsors: International Petroleum Technology Institute and the Pipeline Division
  • ISBN: 978-0-7918-4858-6 | eISBN: 798-0-7918-3835-8
  • Copyright © 2008 by ASME

abstract

The tests of fatigue crack overload retardation were performed to gain a some what deeper understanding of overload retardation. We present an experimental investigation of fatigue crack retardation behavior caused by intermediate single peak tensile overload under constant amplitude cyclic loading. The compact tension (CT) specimens of API grade X80 pipeline steel were used in fatigue test. The results show there was an instant crack extension during overloading for the tested overload ratios. As soon as the overload cycle was removed, instant delay in crack growth occurred. The results should be of interest for fracture mechanics prediction models on fatigue crack growth under variable amplitude loading and overloading effect for oil and gas pipelines.

Copyright © 2008 by ASME
Topics: Steel , Fatigue cracks

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In