Investigation of Board-Level and Package-Level Drop Reliability of RF MEMS Packages

[+] Author Affiliations
Li Sun, Dana DeReus, Shawn Cunningham, Arthur Morris

Wispry, Inc., Irvine, CA

Paper No. IMECE2009-11741, pp. 225-230; 6 pages
doi:10.1115/IMECE2009-11741
From:
  • ASME 2009 International Mechanical Engineering Congress and Exposition
  • Volume 5: Electronics and Photonics
  • Lake Buena Vista, Florida, USA, November 13–19, 2009
  • Conference Sponsors: ASME
  • ISBN: 978-0-7918-4378-9 | eISBN: 978-0-7918-3863-1
  • Copyright © 2009 by ASME

abstract

Board-level and package-level drop reliability is of critical importance for RF MEMS packages. In this paper, we present a numerical study of reliability of RF MEMS packages during board-level and package-level drop testing. The RF MEMS package consists of a 3.8 mm × 2.5 mm × 0.5 mm RF MEMS die flip-chip assembled on a 5.2 mm × 5.2 mm × 0.4 mm LTCC substrate using lead-free solder balls and a metal lid soldered down on the LTCC substrate to cover the RF MEMS die. The board-level and package-level drop modeling were conducted in accordance with JEDEC standards JESD22-B111 and JESD22-B110A, respectively. The support excitation method was employed to investigate the transient response of the packages. With board-level drop modeling, it was found that the maximum peeling stress in the land grid array (LGA) on the test board side was approximately 170 MPa when the package was mounted on the test board center, and LGA stress reduced to approximately 80 MPa when the package was mounted on the test board edge. As high peeling stress may cause fracture of the intermetallic compound in the solder, the modeling result suggests that the RF MEMS package be placed near the board edge or pins in handheld electronic products. A parametric study of the impact, peak acceleration and pulse duration, was also conducted. It was observed that the maximum stress increased with higher peak acceleration. The maximum stress, however, did not vary monotonically with pulse duration. Package-level drop modeling revealed that the failure of the RF MEMS package would be primarily driven by the inertial force. The transient response of the package synchronized with the drop impact. The maximum stress in the package did not appear in the solder balls but in the seal ring that connects the metal lid to the LTCC substrate. The modeling result indicates that it is important to carry out hermeticity tests before and after package-level drop tests to ensure the package integrity.

Copyright © 2009 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In