Friction and Wear of Bronze Filled PTFE and Graphite Filled PTFE in 40 MPA Hydrogen Gas

[+] Author Affiliations
Yoshinori Sawae, Shunichiro Doi, Hideki Watanabe, Yoshie Kurono

Kyushu University, Fukuoka, Japan

Eiichi Miyakoshi, Joichi Sugimura

The National Institute of Advanced Industrial Science and Technology, Fukuoka, Japan

Paper No. IJTC2011-61215, pp. 249-251; 3 pages
doi:10.1115/IJTC2011-61215
From:
  • ASME/STLE 2011 International Joint Tribology Conference
  • ASME/STLE 2011 Joint Tribology Conference
  • Los Angeles, California, USA, Oct 24–26, 2011
  • ISBN: 978-0-7918-5474-7
  • Copyright © 2011 by ASME

abstract

Several kinds of Polytetrafluoroethylene (PTFE) composites are currently being used in reciprocating hydrogen gas compressors as seal material which should articulate against metal counterfaces in pressurized hydrogen gas. Although their friction and wear behavior has large impact on the efficiency and reliability of gas compressors, available information about tribological characteristics of PTFE composites in high pressure hydrogen gas is quite limited. In this study, friction and wear of graphite filled PTFE and bronze filled PTFE were evaluated in the 40 MPa hydrogen gas environment by using a pin-on-disk type apparatus enclosed in a high pressure vessel to supply experimental data for the design of gas compressors in hydrogen fuelling stations. AISI316L austenitic stainless steel disk was used as a sliding counterface. All experiments were conducted under dry condition with the average contact pressure of 1.8 MPa, the sliding speed of 100 mm/s and the gas temperature of 327 K. The friction force exerted between PTFE composites and stainless steel was evaluated by a load cell during the experiment and the wear rate of composites was evaluated from the weight loss of pin specimens. In addition, chemical analysis of the polymer transfer film formed on the disk surface were conducted by using X-ray photoelectron spectrometer. Friction and wear tests were also conducted in 40 MPa helium gas for comparison. Results indicated that bronze filled PTFE was more sensitive to the gas pressure and gas species; it showed good friction and wear behavior in high pressure hydrogen, although friction in high pressure helium became very high. On the other hand, the effects of high pressure gas environment were relatively small for the friction and wear of graphite filled PTFE.

Copyright © 2011 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In