Summary of Weld Residual Stress Analyses for Dissimilar Metal Weld Nozzles

[+] Author Affiliations
F. W. Brust, Tao Zhang, Do-Jun Shim, Sureshkumar Kalyanam, Gery Wilkowski

Engineering Mechanics Corporation of Columbus, Columbus, OH

Mike Smith, Andrew Goodfellow

British Energy Generation Limited (UK), Barnwood, Gloucester, UK

Paper No. PVP2010-26106, pp. 1521-1529; 9 pages
doi:10.1115/PVP2010-26106
From:
  • ASME 2010 Pressure Vessels and Piping Division/K-PVP Conference
  • ASME 2010 Pressure Vessels and Piping Conference: Volume 6, Parts A and B
  • Bellevue, Washington, USA, July 18–22, 2010
  • Conference Sponsors: Pressure Vessels and Piping Division
  • ISBN: 978-0-7918-49255 | eISBN: 978-0-7918-3878-5
  • Copyright © 2010 by ASME

abstract

Flaw indications have been found in some dissimilar metal nozzle to stainless steel piping welds in pressurized water reactors (PWR) throughout the world. The nozzle welds usually involve welding ferritic (often A508) nozzles to 304/316 stainless steel pipe using Alloy 182/82 weld metal. Due to an unexpected aging issue with the weld metal, the weld becomes susceptible to a form of corrosion cracking referred to as primary water stress corrosion cracking (PWSCC). It can occur if the temperature is high enough (usually >300C) and the water chemistry in the PWR is typical of operating plants. This paper represents one of a series of papers which examine the propensity for cracking in a particular operating PWR in the UK. This paper represents an examination of the weld residual stress distributions which occur in four different size nozzles in the plant. Companion papers in this conference examine crack growth and PWSCC mitigation efforts related to this plant. British Energy (BE) has developed a work program to assess the possible impact of PWSCC on dissimilar metal welds in the primary circuit of the Sizewell ‘B’ pressurized water reactor. This effort has included the design and manufacture of representative PWR safety/relief valve nozzle welds both with and without a full structural weld overlay, multiple residual stress measurements on both mock-ups using the deep hole and incremental deep hole methods, and a number of finite element weld residual stress simulations of both the mock-ups and equivalent plant welds. This work is summarized in companion papers [1–3]. Here, the detailed weld residual stress predictions for these nozzles are summarized. The weld residual stresses in a PWR spray nozzle, safety/relief nozzle, surge nozzle, and finally a steam generator hot-leg nozzle are predicted here using an axis-symmetric computational weld solution process. The residual stresses are documented and these feed into a natural crack growth analysis provided in a companion PVP 2010-25162 paper [1]. The solutions are made using several different constitutive models: kinematic hardening, isotropic hardening, and a mixed hardening model. Discussion will be provided as to the appropriateness of the constitutive model for multi-pass DM weld modeling. In addition, the effect of including or neglecting the post-weld heat treatment process, which typically occurs after the buttering process in a DM weld, is presented. During operation the DM welds in a PWR experience temperatures in excess of 300°C. The coefficient of thermal expansion (CTE) mismatch between the three materials, particularly the higher CTE in the stainless steel, affects the stresses at operating temperature. The K-weld geometry used in the steam generator nozzles in this plant combines with CTE mis-match effects to result in service stresses somewhat different from V-weld groove cases.

Copyright © 2010 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In