Corrosion Behaviors of Al-Steel-Sputtering-Treated Steel and SiC/SiC Composites in High Temperature LBE at Low Oxygen Concentration

[+] Author Affiliations
Abu Khalid Rivai, Minoru Takahashi

Tokyo Institute of Technology, Tokyo, Japan

Paper No. ICONE14-89303, pp. 477-482; 6 pages
  • 14th International Conference on Nuclear Engineering
  • Volume 1: Plant Operations, Maintenance and Life Cycle; Component Reliability and Materials Issues; Codes, Standards, Licensing and Regulatory Issues; Fuel Cycle and High Level Waste Management
  • Miami, Florida, USA, July 17–20, 2006
  • Conference Sponsors: Nuclear Engineering Division
  • ISBN: 0-7918-4242-8 | eISBN: 0-7918-3783-1
  • Copyright © 2006 by ASME


Corrosion tests of Al and SS-304-sputtering-surface treated STBA26 (9Cr.1Mo.0.1Si) and SiC/SiC composites with BN (boron nitide) coating has been conducted in high temperature LBE of 700°C at low oxygen concentration of 6.8 × 10−7 wt% and the behavior was analyzed. The sputtering technique was used to protect the steel from corrosion. The thickness of sputtering-treated layer was 21.45 μm. All specimens were immersed in LBE in a pot for 1000 hours. The STBA26 (9Cr.1Mo.0.1Si) without surface treated were also tested for comparison with sputtering-treated steels. The results showed that sputtering-treated layer still remained on the base of STBA26. No penetration of LBE was observed in this layer. The layer could protect the steel from penetration of LBE. The result also showed that thin layer which contains aluminum oxide and chromium oxide was formed on the surface-treated layer, and it protected the base area. On the contrary, the penetration in base area was observed in the as received STBA26. In SiC/SiC composites, there appeared cracks in a thin surface area and LBE penetrated deeply into the material. The corrosion did not occur in this SiC/SiC composite in the high temperature LBE.

Copyright © 2006 by ASME



Interactive Graphics


Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In