Direct Carbon Fuel Cell With Hydroxide Electrolyte: Cell Performance During Initial Stage of a Long Term Operation

[+] Author Affiliations
S. Zecevic, E. M. Patton, P. Parhami

Scientific Applications & Research Associates (SARA), Inc., Cypress, CA

Paper No. FUELCELL2005-74169, pp. 507-514; 8 pages
doi:10.1115/FUELCELL2005-74169
From:
  • ASME 2005 3rd International Conference on Fuel Cell Science, Engineering and Technology
  • 3rd International Conference on Fuel Cell Science, Engineering and Technology
  • Ypsilanti, Michigan, USA, May 23–25, 2005
  • Conference Sponsors: Nanotechnology Institute
  • ISBN: 0-7918-3764-5 | eISBN: 0-7918-3757-2
  • Copyright © 2005 by ASME

abstract

This paper describes a Direct Carbon-Air Fuel Cell (DCFC) which uses a molten hydroxide electrolyte. In DCFCs, carbon is electrochemically directly oxidized to generate the power without a reforming process. Despite its compelling cost and performance advantages, the use of molten metal hydroxide electrolytes has been ignored by DCFC researches, primarily due to the potential lack of invariance of the molten hydroxide electrolyte caused by its reaction with carbon dioxide. This paper describes the electrochemistry of DCFC based on molten hydroxide electrolyte and discusses means to overcome the historical carbonate formation. Furthermore, it describes the cell performance during the initial stage of a long term operation and discusses the causes for the initial cell performance degradation. To date, five successive generations of medium temperature DCFC prototypes have been built and tested at SARA Inc. to demonstrate the technology, all using graphite rods as their fuel source. The basic feature of the cell is a simple design in which the cathode is not traditional gas fed electrode type. It is a non-porous electrode structure made of an inexpensive Fe-Ti alloy and gaseous oxygen is introduced into the cell by bubbling humid air through the electrolyte. The cell successfully demonstrated delivering more than 50 A at 0.3 V with the current density exceeding 100 mA/cm2 . Main feature of DCFC with hydroxide electrolyte is that the cell performance decreases over time mainly due to oxygen cathode polarization. There are three possible causes for this performance decay: Carbonate formation, electrolyte evaporation due to air bubbling, and corrosion products build up. In order to determine the right cause for the performance decay a series of experiments was carried out investigating various parameters involving cell temperature, water content in the melt, current density, carbonate content in the melt, melt level in the cell, air flow rate and intermittent on-off operation. DCFC was operating at constant current while cell voltage and electrode potentials were recorded over time. Results obtained indicated that the performance of DCFC with hydroxide electrolyte during initial 200 h is governed by the oxygen cathode performance that is mainly affected by corrosion products. The corrosion products catalyze decomposition of peroxide ions which are reacting species at the cathode resulting in an increase of cathode polarization over time. Effect of carbonate ions on the initial cell performance decay is insignificant as compared to the effect of corrosion product. Means to overcome the corrosion products issue were discussed.

Copyright © 2005 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In