Testing of Fracture Toughness Under Biaxial Loading

[+] Author Affiliations
Milan Brumovsky, Jiri Palyza

Nuclear Research Institute Rez plc, Rez, Czech Republic

Dana Lauerova

Nuclear Research Institute Rez ply, Rez, Czech Republic

Paper No. PVP2005-71479, pp. 183-186; 4 pages
doi:10.1115/PVP2005-71479
From:
  • ASME 2005 Pressure Vessels and Piping Conference
  • Volume 6: Materials and Fabrication
  • Denver, Colorado, USA, July 17–21, 2005
  • Conference Sponsors: Pressure Vessels and Piping Division
  • ISBN: 0-7918-4191-X | eISBN: 0-7918-3763-7
  • Copyright © 2005 by ASME

abstract

Reactor pressure vessels under some special regimes (i.e. pressurized thermal shock) are loaded by a strongly biaxial tensile stresses whose ratio can reach even an opposite value in comparison with normal operating conditions. Pressure vessel integrity as well as its life assessment is performed on the basis of fracture mechanics where normally only uniaxial fracture toughness of materials are used as material inputs. Special biaxial tests on cruciform type specimens with thickness up to 90 mm were tested in Nuclear Research Institute (NRI) Rez - special testing equipment and testing methods including measurements have been developed and realized. Testing equipment with maximum loading up to 1.5 MN allows to reach different biaxial loading ratios between 0 and 2. During tests, carried out mostly at low temperatures, specimens deflections, strains, load and crack opening displacement are measured and then evaluated. In NRI Rez comparative experimental tests on cruciform and beam specimens were performed. The aim of these tests was to examine the effect of crack depth and biaxial loading on fracture toughness for reactor pressure vessel material 15Kh2MFA. For evaluating the tests, the FEM (program SYSTUS) was used. The performed tests confirm shallow crack effect, i.e. increase of fracture toughness for shallow cracks compared to that one of deep cracks. Further, the performed experiments show decrease of fracture toughness of shallow cracks loaded biaxially compared to uniaxial loading of shallow cracks. Quantitatively, the fracture toughness decrease was about 20%.

Copyright © 2005 by ASME

Figures

Tables

Interactive Graphics

Video

Country-Specific Mortality and Growth Failure in Infancy and Yound Children and Association With Material Stature

Use interactive graphics and maps to view and sort country-specific infant and early dhildhood mortality and growth failure data and their association with maternal

NOTE:
Citing articles are presented as examples only. In non-demo SCM6 implementation, integration with CrossRef’s "Cited By" API will populate this tab (http://www.crossref.org/citedby.html).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In